Product Details:
|
| Properties: | Anti-corrosion | Feature: | High Elongation And Tensile Strenght |
|---|---|---|---|
| Elongation: | 400% | Adhesion: | 20MPa |
| Hard Dry Time: | 12h | Touch Dry Time: | 4h |
| Highlight: | Air Dry Polyaspartic Guide Formulation,Anti Corrosion Polyaspartic Guide Formulation |
||
Windmill Blade Leading Edge 2 Polyaspartic Guide Formulation
| Windmill Blade Leading Edge 2 Polyaspartic Guide Formulation | |||||||
| Curing method | Air Dry | ||||||
| Application | Fiberglass substrate windmill blade leading edge protective coat | ||||||
| Characters | High solid low VOC, high elongation and tensile strength, good rain erosion and weather resistance, excellent flexibility in low temperature, Good performance retention after aging. | ||||||
| A component | B component | ||||||
| Material | Content | Supplier | Process | Material | Content | Supplier | |
| F420 | 36 | Feiyang | Grind to fineness≤30um | Tolonate HDT LV | 8 | Vencorex | |
| dispersing agent | 1 | worthchem | GB925-85 | 85.5 | Feiyang | ||
| titanium dioxide | 45.5 | CA | N-butyl acetate | 6 | CA | ||
| 3A molecular sieve | 5 | CA | Water absorbent | 0.5 | CA | ||
| anti-setting agent | 0.4 | CA | |||||
| N-butyl acetate | 10 | CA | |||||
| 1130 | 1 | CA | |||||
| 292 | 0.5 | CA | |||||
| Defoamer | 0.4 | CA | |||||
| Leveling agent | 0.2 | CA | |||||
| Total | 100 | Total | 100 | ||||
| Ratio: 1:1 by quantity | |||||||
| Specifications | Remarks | ||||||
| Pot life | 40m | ||||||
| Solid content | 85% | ||||||
| Touch dry time | 4 h | ||||||
| Hard dry time | 12h | ||||||
| Hardness | |||||||
| Elongation | 400% | ||||||
| Adhesion, MPa | 20 | ||||||
| QUVB | 3000h | ||||||
| wear value CS17, 500g500r,mg | 6 | ||||||
| SHENZHEN FEIYANG PROTECH CORP., LTD | |||||||
| Feiyang Tech-Park, 8 Longchang Road, Bao'an Dist, 518101 Shenzhen, GD, China | |||||||
Learn polyaspartic knowledge: Polyaspartic FAQ
Contact Person: Annie Qing
Tel: +86 18307556691
Fax: 86-183-07556691