Product Details:
|
| Pot Life: | 30min | Solid Content: | 93 |
|---|---|---|---|
| Touch Dry Time: | 3h | Hard Dry Time: | 24h |
| Thickness: | 0.1 | Hardness: | H |
| High Light: | Non Yellowing Polyaspartic Thin Coating,93 Polyaspartic Thin Coating,ISO 14001 Polyaspartic Thin Coating |
||
Polyaspartic Non-yellowing Thin Coating Finish
| Formula Name: Polyaspartic Thin Coating | |||||||
| Component | Polyaspartic resins and HDI trimer hardener | ||||||
| Curing method | Cure at normal temperature | ||||||
| Characters | Weather resistance, non-yellowing, high solid content | ||||||
| A component | B component | ||||||
| Material | Content | Supplier | Process | Material | Content | Supplier | |
| F520 | 30 | Feiyang | Mix at room temperature | HDT-LV2 | 80 | vendors | |
| dispersing agent BYK163 | 1 | BYK | EGDA | 20 | FEIYANG | ||
| fumed silica HDK-N20 | 0.5 | WACKER | |||||
| water absorbent oxazolidine | 1 | ICL | |||||
| defoamer BYK1790 | 0.3 | WACKER | |||||
| Barium sulfate 605 | 21.9 | From China | |||||
| pigment | 8 | From China | |||||
| F2850 | 12 | Feiyang | |||||
| F420 | 4 | Feiyang | |||||
| F520 | 16 | Feiyang | |||||
| 3A activation powder | 5 | From China | |||||
| flatting agent BYK358 | 0.3 | BYK | |||||
| Total | 100 | Total | 100 | ||||
| Ratio:A: B=2:1 | |||||||
| Specifications | Construction Description | ||||||
| Pot life | 30min | Construction by roller. If humidity＞85%, stop construction. Thickness is no more than 0.2mm; otherwise will cause bubbles. |
|||||
| Solid content | 93 | ||||||
| Touch dry time 25℃ | 3hr | ||||||
| Hard, dry time 25℃ | 24hr | ||||||
| Thickness | 0.1 | ||||||
| Hardness | H | ||||||
| Elongation | -- | ||||||
| Tensile strength | -- | ||||||
| Resilience force | -- | ||||||
| Glasses | 90 | ||||||
Learn polyaspartic knowledge: Polyaspartic FAQ