DESMODUR N3300 Isocyanate HT 100,
Hardener Component Isocyanate HT 100,
Hardener Component DESMODUR N3300
Aliphatic polyisocyanate (HDI trimer).
As the hardener component for lightfast polyurethane coating systems.
|Property||Value||Unit of measurement||Method|
|NCO content||21.8 ± 0.3||%||DIN EN ISO 11 909|
|Viscosity at 23 °C||3,000 ± 750||mPa·s||DIN EN ISO 3219/A.3|
|Color value (Hazen)||≤ 40||DIN EN 1557|
|Monomeric HDI||< 0.15||%||DIN EN ISO 10 283|
|Viscosity at 25 °C||approx. 2,500||mPa·s||DIN EN ISO 3219/A.3|
|Equivalent weight||approx. 193|
|Flash point||approx. 228||°C||DIN 22 719|
|Density at 20 °C||approx. 1.16||g/ml||DIN EN ISO 2811|
3. Solubility / thinnability
Desmodur® N 3300 can be thinned with esters, ketones, and aromatic
hydrocarbons such as ethyl acetate, butyl acetate, methoxy propyl acetate, acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, toluene,
xylene, solvent naphtha® 100, and mixtures thereof.
Generally speaking, it has good compatibility with the solvents listed. However, the solutions formed must be tested for their storage stability. Only PU-grade solvents should be used (max. 0.05 % water, absence of reactive hydroxyl or amino groups). Aliphatic hydrocarbons are unsuitable as solvents.
Desmodur® N 3300 should not be thinned below a solids content of 40 %. Prolonged solution storage with a lower binder content may result in turbidity and sedimentation.
Generally speaking, Desmodur® N 3300 can be mixed with the following products: aliphatic polyisocyanates such as Desmodur® N 100, N 75, N 3200, N 3400, N 3600 and Desmodur® Z 4470; aromatic polyisocyanates such as Desmodur® L, HL, and IL; polyester polyols such as Desmophen® 670;
polyacrylates such as the Desmophen® A products. However, the compatibility of the combinations used should constantly be tested.
Desmodur® N 3300 is incompatible with branched polyester polyols such as Desmophen® 651 or polyether polyols such as Desmophen® 1380 BT.
5.Properties / Applications
Desmodur® N 3300 is primarily the hardener component for lightfast
two-component polyurethane coatings with high chemical and weather resistance, good gloss retention, and outstanding mechanical properties. Preferred co-reactants are polyacrylate or polyester polyols.
The main applications for systems based on Desmodur® N 3300 are air- and force-drying coatings for automotive OEM, automotive refinishing, transportation, industrial finishing, and plastics.
- Storage in original sealed Covestro container.
- Recommended storage temperature: 10 - 30 °C.
- Protect from moisture, heat, and foreign material.
General information: The product is sensitive to moisture and should therefore be stored in tightly sealed containers. Storage at elevated temperatures will lead to an increase in viscosity and a reduction of the NCO content.