Product Details:
|
| Model: | GB905A-85 | Origin: | Zhuhai,China |
|---|---|---|---|
| Appearance: | Transparent Liquid | NCO Content: | 6.6-7.2% |
| Viscosity Mpa.s/25°C: | 3000-6000 | Feature: | High Weathering Resistance |
| Highlight: | High Strength Elastic Polyurea Curing Agent,FEICURE Elastic Polyurea Curing Agent |
||
FEICURE GB905A-85 High Elastic Isocyanate Harder
PROFILE
FEICURE GB905A-85 is a kind of aliphatic isocyanate prepolymer curing agent modified by two functional and linear polyester.
PROPERTY
APPLICATIONS
INDEX
| INDEX | VALUE |
| Appearance | Colorless to light yellow transparent liquid |
| Hazen (Pt-Co) | ≤150 |
| Solid Content(％) | 85±2(in XYL) |
| NCO Content(％) | 6.6～7.2 |
| Viscosity(mpa.s/25℃) | 3000～6000 |
| Relative density (25℃) | 1.07±0.02 |
PACKING
200 Kgs/Drum, 10 Kgs/Drum
SHELF LIFE
FEICURE GB905A-85 must be stored in airtight containers to prevent contact with moisture. Recommended storage temperature is 0℃-30℃ (32℉-86℉). The shelf life in the closed original container is 12 months.
NOTICE
FEICURE GB905A-85 is combustible and should be stored at the temperature at 0℃- 30°C. It should be kept away from fire source and stored in a cool, dry and ventilated environment. The storage period is 12 months.
The coating formulated with FEICURE GB905A-85 should be tested for performance after one week’s maintenance.
Note: This manual is for reference only, without any warranty. In view of the limitation of resin function and the diversity of user requirements, please strictly test the adaptability of the product and the stability of the final product. The technical information is subject to change without prior notice.
FEICURE Isocyanate Hardener
| Models | Relative Density (25℃) | Viscosity (mpa.s/25℃) | Solid Content % | NCO Content | Type |
| SP-103P | 1.01 | 100-200 | 60 in BA | 3.2-3.6 | IPDI Prepolymer |
| GB905A-85 | 1.05 | 3000-6000 | 85 in Xylene | 6.6-7.2 | IPDI Prepolymer |
| GB925-85 | 1.05 | 4000-6000 | 85 in BA | 4.9-5.3 | IPDI Prepolymer |
| GB926A-85 | 1.05 | 4000-6000 | 80 in Xylene | 4.9-53 | IPDI Prepolymer |
| GB805A-100 | 1.1 | 3000-6000 | ≧99 | 4.7-5.2 | TDI/HMDI Prepolymer |
| GB805B-100 | 1.05 | 1500-3000 | ≧98 | 10.3-10.7 | TDI/HMDI Prepolymer |
Learn polyaspartic knowledge: Polyaspartic FAQ
Contact Person: Annie Qing
Tel: +86 18307556691
Fax: 86-183-07556691